Product specification
Customer :
Model : EPT SCP2000mAh
Prepared by : Yuan Miao Mo
Audit by :
Approved by :
Add :Blok-31,33 tongfucun Industrial District, Dalang Village , Shenzhen City , China Post Code:518109 Tel: 0755-******** 28078030 28078363 Fax:0755-******** 深圳市量能科技有限公司
EPT BATTERY (SHENZHEN )CO.,LTD
Type Rechargeable Nickel Metal
Hydride Battery
Model EPT SCP2000mAh
Cell Size SC
Nominal voltage 1.2V
Typical Weight about 45g(ref)
Capacity (20℃, discharge at 0.2Cto ccv=1.0V)
Typical 2030mAh(ref)
Minimum 2000mAh
Charge condition(20℃)
Charging Condition charge at 0.1 C for16h
Fast Charge 1000mA~2000mA (0.5Cto1C)
DT/dt:0.8℃~0.9℃/min(0.5C)
DT/dt:0.9℃~1℃/min(1C)
T MAX=65 ℃
/time: charge capacity reach to
105% nominal capacity/
Trickle charge 100mA ~200mA
Max over-charge current 0.1 C charge for 48 hrs
Discharge condition
Discharge cut off voltage 1.0V
Maximum Discharge Current 6000 mA(3C)
Storage Temperature(65±20%RH)
Storage(1year)-20℃~25℃
Storage(six month)-20℃~35℃
Storage(1 month)-20℃~45℃
Storage(7days)-20℃~55℃
Operation temperature(Relative humidity:65±20%RH)
Discharge -20℃~60℃
Charge 0℃~45℃
Fast charge 10℃~45℃
Trickle charge 0℃~45℃
1、PERFORMANCE
Unless otherwise stated, tests should be done within one month of delivery under the following conditions
Ambient Temperature:20±5℃Relative Humidity:65±20%RH Notes: Standard Charge/Discharge Condition:
Notes:
1. Approximate charge time from discharged rate, for reference only IEC 61951-2(2011)IEC61951-2(2011)/7.5.1.2Cycle Life Test:
2. EXTERNAL APPEARANCE
The cell / battery shall be free from cracks, scars, breakage, rust, discoloration, leakage and deformation.
3. ELECTRICITY RETAINS:
Normal conditions with electricity retain 50%, if have special demands, confirm after negotiate.
4. WARRANTY
One year limited warranty against workmanship and material defects.
5. WARRANTY
5.1 Do not reverse charge batteries.
5.2 Do not short circuit batteries, permanent damage to batteries may result.
5.3 Do not subject batteries to adverse condition such as extreme temperature, deep cycling
and excessive.
5.4 Store batteries in a cool dry place. Always discharge batteries before bulk storage or
shipment.
5.5 Do not solder directly to cells or batteries.
5.6 If find any noise, excessive temperature or leakage from a battery, please stop its use.
5.7 Do not incinerate or mutilates batteries, may burst or release toxic material.
5.8 Do not mix new batteries in use with semi-used batteries, over-discharge may occur.
5.9 Do not remove the outer sleeve from a battery pack nor cut into its housing.
5.10 Never put a battery into water or seawater.
6. CAUTION
6.1 Batteries should be charged prior to use.
6.2 For charging methods please referred to our technical handbook.
6.3 Use the correct charger for Ni-MH batteries.
6.4 Avoid batteries being used in an airtight compartment. Ventilation should be provided inside
the battery compartment, otherwise batteries may generate hydrogen gas, which could cause an explosion if exposed to an ignition source.
6.5 Do not attempt to take batteries apart or subject them to pressure or impact. Heat may be
generated or fire may result. The alkaline electrolyte is harmful to eyes and skin, and it may damage clothing upon contact.
6.6 Keep away from children. If swallowed, contact a physician at once.
6.7 When using a new battery for the first time or after long term storage, please fully charge the
battery before use.
6.8 When using a new battery in use with semi-used batteries, over-discharge may occur.
6.9 When the battery is hot, please do not touch it and handle it, until it has cooled down.
6.10 When find battery power down during use, please switch off the device to avoid over
discharge.
6.11 Unplug a battery by holding the connector itself and not by pulling at its cord.
6.12 After use, if the battery is hot. Before recharging it, allow it to cool in a well-ventilated place
out of direct sunlight.
7、STORAGE
7.1 In order to ensure the battery to maintain the capacity level, We suggest Ni-MH battery and
battery pack should be stored under the condition of the -20 ~ 35 ℃, low humidity, no
corrosive gases.
7.2 Ni-MH battery to avoid the high temperature or high humidity storage, otherwise it would
lead to the battery leakage, rust, and the lower capacity
7.3 The long-term storage may lead to NIMH batteries and battery packs to reduce the capacity
and need 1-3 charge / discharge cycles to reach the maximum discharge capacity.
7.4 Three months after placing the battery need to be charge/discharge for one cycle.
(With sleeve) H=43.0mm
Applications: Recommended discharge current 200mA to 6000mA Nominal Voltage: 1.2V Capacity:
Minimum: 2000mAh Typical: 2030mAh
When discharged at 0.2C to 1.0V at 20℃ Charging Condition: 200mA for 16 hrs at 20℃ Fast Charge : 1000mA to 2000mA (0.5Cto1C)
Charge termination control recommended
Control parameters: △V: 5mV
DT/dt:0.8℃~0.9℃/min(0.5C) DT/dt:0.9℃~1℃/min(1C) T MAX =65 ℃ Time: 105% nominal input
For reference only Service life: ≥500 cycles (IEC standard) Continuous: 200mA maximum current for 48 hrs Overcharge:
No conspicuous deformation
And/or leakage
Weight: about 45g
Internal Resistance: Max 20mΩ upon fully charged 1C 0.5C Capacity input (%)
Charge0.1C*16hrs at20℃ Low rate discharge
Voltage (V)
(0.2C) (0.1C) (0.5C)