LUPOY1201-10P

Technical Information

LUPOY PC 1201-10P

Polycarbonate Resin

Introduction

LUPOY PC 1201-10P resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. Main Characteristics ? FDA 1

? Medium viscosity ? Good mold release

Applications

? Toys

? Food utensils

? Packaging applications

Properties 2 Test English

SI

Method Value Units Value Units Physical

Melt Flow Rate (300 °C /1.2 kg) ASTM D 1238 10 g/10 min 10 g/10 min Density

ASTM D 792 1.20

1,200

kg/m 3 Mold Shrinkage

ASTM D 955 0.005～0.007 in/in 0.005～0.007 mm/mm Water Absorption @ 24 hrs, 23°C

ASTM D 570 0.15 % 0.15 % @ equilibrium, 50%RH, 23°C ASTM D 570 0.32 % 0.32 % Optical

Refractive Index, n D ASTM D 542 1.586 1.586 Light Transmittance ASTM D 1003 89 % 89 % Haze ASTM D 1003

0.7～1.5 % 0.7～1.5 % Thermal

Deflection Temperature Under Load (DTUL) @ 4 mm @ 66 psi (0.45 MPa), annealed @ 264 psi (1.8 MPa), annealed @ 264 psi (1.8 MPa), unannealed

ASTM D 648 291 286 262 °F °F °F 144 141 128 °C °C °C Vicat Softening Point, 50°C /hr, 50N Load

ASTM D 1525 300 °F 149 °C

Coefficient of Linear Thermal Expansion, @ -40 to 82°C ASTM D 696 38 x 10-6 in/in/°F 68 x 10-6 mm/mm/°C Mechanical

Tensile Yield Strength 3 ASTM D 638 8,700 psi 60 MPa Ultimate Tensile Strength ASTM D 638 10,300 psi 71 MPa Elongation at Yield ASTM D 638 6 % 6 % Elongation at Break ASTM D 638 150 % 150 % Tensile Modulus ASTM D 638 350,000 psi 2,410 MPa Flexural Strength ASTM D 790 14,000 psi 96 MPa Flexural Modulus

ASTM D 790 350,000 psi 2,410 MPa Notched Izod Impact 4 @ 23 °C ASTM D 256 17

ft-lb/in 900 J/m Unnotched Izod Impact @ 23 °C

ASTM D 256 No break No break Instrumented Dart Impact 5, Total Energy @ 23 °C ASTM D 3763 770 in-lb 87 J

Rockwell Hardness

ASTM D 785 118 R Scale 73 M Scale Taber Abrasion Resistance 6 (? Haze) ASTM D 1044 45 % 45 % Ignition Resistance 7 UL-94 @ 0.5 mm ASTM D635 V-2 V-2 UL-94 @ 1.6 mm ASTM D635 V-2 V-2 UL-94 @ 2.5-2.7 mm ASTM D635 V-2 V-2 UL-94 @ 3.0 mm ASTM D635 HB HB Limiting Oxygen Index

ASTM D 2863 26 % 26 % Ball Indentation Temperature IEC 598-1 >125 °C >125 °C Average Extent of Burning ASTM D 635 1 in 25 mm Electrical

GWT 2.0 mm, 5 second

IEC 695-2-1 850 °C 850 °C Comparative Tracking Index @ 2.0 mm IEC 112 250 V 250 V

Dielectric Strength

ASTM D 149 420 V/mil 17 KV/mm Dielectric Constant @ 60 Hz ASTM D 150 3 3 Dissipation Factor @ 60 Hz ASTM D 150 0.001

0.001

Volume Resistivity @ 23 °C, dry

ASTM D 257

2.0 x 1017

?-cm

2.0 x 1017

?-cm

1. When used unmodified for the manufacture of food contact articles LUPOY 1201-10 Polycarbonate resins comply with the U.S. Food, Drug, and Cosmetic Act and Food Additive Regulations 21 CFR 177.1580 and E.U. Food Contact Regulations. The uses cited above are subject to GMP (Good Manufacturing Practices) and any limitations that are part of the regulations.The regulations should be consulted for complete details.

2. Typical properties; not to be constructed as specifications.

3. Tensile Test @ 23 °C; 50 mm/min.

4. 0.125 in; 10 mil notch (3.2 mm; 0.25 mm notch).

5. 0.125 in; 8000 ipm (3.2 mm; 203 m/min).

6. 1,000 g; CS-10 F wheel; 500 cycles.

7. These numerical flame spread ratings are small-scale test values and are not intended to reflect hazards presented by these or any other materials under actual fire conditions. UL 94 file: E306922.